Title: The fracture toughness of soft tissues
Author: SIMMS, CIARAN KNUT
TAYLOR, DAVID
Author's Homepage: http://people.tcd.ie/blucey
http://people.tcd.ie/csimms
http://people.tcd.ie/dtaylor
Keywords: Bioengineering
Fracture Toughness
Issue Date: 2012
Publisher: Elsevier
Citation: David Taylor, Niamh O'Mara, Eoin Ryan, Michael Takaza, Ciaran Simms, The fracture toughness of soft tissues, Journal of the Mechanical Behavior of Biomedical Materials, 6, 2012, 139-147
Series/Report no.: Journal of the Mechanical Behavior of Biomedical Materials;
6;
Abstract: Fracture toughness is important for any material, but to date there have been few investigations of this mechanical property in soft mammalian tissues. This paper presents new data on porcine muscle tissue and a detailed analysis of all previous work. The conclusion is that, in most cases, fracture toughness has not in fact been measured for these tissues. Reanalysis of the previous work shows that failure of the test specimens generally occurred at the material’s ultimate strength, implying that no information about toughness can be obtained from the results. This finding applied to work on cartilage, artificial neocartilage, muscle and the TMJ disc. Our own data, which was also found to be invalid, gave measured fracture toughness values which were highly variable and showed a strong dependence on the crack growth increment. The net-section failure stress and failure energy were relatively constant in large specimens, independent of crack length, whilst for smaller specimens they showed a strong size effect. These findings are explained by the fact that the process zone size, estimated here using the critical distance parameter L, was similar to, or larger than, critical specimen dimensions (crack length and specimen width). Whilst this analysis casts doubt on much of the published literature, a useful finding is that soft tissues are highly tolerant of defects, able to withstand the presence of cracks several millimetres in length without significant loss of strength.
Description: PUBLISHED
URI: http://hdl.handle.net/2262/61669
Related links: http://dx.doi.org/10.1016/j.jmbbm.2011.09.018
Appears in Collections:Mechanical & Manufacturing Eng (Scholarly Publications)

Files in This Item:

File Description SizeFormat
The fracture toughness of soft tissues.pdfPublished (author's copy) - Peer Reviewed1.52 MBAdobe PDFView/Open


This item is protected by original copyright


Please note: There is a known bug in some browsers that causes an error when a user tries to view large pdf file within the browser window. If you receive the message "The file is damaged and could not be repaired", please try one of the solutions linked below based on the browser you are using.

Items in TARA are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - Feedback