Martin Schreiber, Tarek Lutz, Gareth P. Keeley, Shishir Kumar, Markus Boese, Satheesh Krishnamurthy and Georg S. Duesberg, Transparent ultrathin conducting carbon films, Applied Surface Science, 256, 21, 2010, 6186-6190
Applied Surface Science; 256; 21;
Ultrathin conductive carbon layers (UCCLs) were created by spin coating resists and subsequently converting them to conductive films by pyrolysis. Homogeneous layers as thin as 3 nm with nearly atomically smooth surfaces could be obtained. Layer characterization was carried out with the help of atomic force microscopy, profilometry, four-point probe measurements, Raman spectroscopy and ultraviolet-visible spectroscopy. The Raman spectra and high-resolution transmission electron microscopy image indicated that a glassy carbon like material was obtained after pyrolysis. The electrical properties of the UCCL could be controlled over a wide range by varying the pyrolysis temperature. Variation in transmittance with conductivity was investigated for applications as transparent conducting films. It was observed that the layers are continuous down to a thickness below 10 nm, with conductivities of 1.6 x 104 S/m, matching the best values observed for pyrolysed carbon films. Further, the chemical stability of the films and their utilization as transparent electrochemical electrodes has been investigated using cyclic voltammetry and electrochemical impedance spectroscopy.
Please note: There is a known bug in some browsers that causes an
error when a user tries to view large pdf file within the browser window.
If you receive the message "The file is damaged and could not be
repaired", please try one of the solutions linked below based on the
browser you are using.
Items in TARA are protected by copyright, with all rights reserved, unless otherwise indicated.